    Guest

    forging

    Does forging a part loaded in uniaxial compression make sense? I can understand forging a part that's under bending or transferring a load around a corner but if it's a straight compression isit worth the time and money? Does anyone have a handle on how to quantify the strength increase in 4340 0r 1045 from forging? And would that be along the grain? Transverse?

  2. #2
    Technical Fellow Kelly_Bramble's Avatar
    Join Date
    Feb 2011
    Location
    Bold Springs, GA
    Posts
    2,625
    Forged parts are beneficial in terms of cyclic loading in any direction. The grain flow structure of a forging is "true" or aligned with the part geometry, where a casting is isotropic or lacking grain direction. In a part manufactured from cold or hot rolled materials the grain flow direction is broken and not aligned with the end-item part geometry.

Tags for this Thread

Posting Permissions

  • You may not post new threads
  • You may not post replies
  • You may not post attachments
  • You may not edit your posts
  •